F 1600/1300 for mud pump liner

1. Name: Ceramic Liner 2. Used for mud pump fluid end 3.10 times life of the ordinary liner.

Our advantages : 

1. Compared with Bi-metal liner and Ceramic liner,the service life of cermet liner is 10 times higher.Its maximum 

and minimum service life can reach more than 5000hours.

2.The reliability is much higher than the Bi-metal and Ceramic liner.

3.The hardness is up to HRC67~HRC70;

4.Compared with the Bi-metal liner and Ceramic liner(is 0.4), the inner face's glabrous of cermet liner is less than 0.1.

5.Bond strength is greater than 110Mpa of metallurgical combine.

6.Friction coefficient of 0.090.(Far below the double metal and ceramic,) the better the life of rubber parts for piston an matching.

7.Does not change the assembly processes of the existing mud pump and double metal cylinder.

8.Cermet compressive strength of is over 2000Mpa.

9.Bending strength is over 1000Mpa

10.Acid: PH1.0~14.0

Cermet Mud Pump Liner:

Latest achievement of military industry civilization 

CAEP (China Academy Engineering Physics) formula and patent

FGM (Functionally Graded Material) and one-step atmosphere sintering process 

Substrate material infiltration, new solution cermet interface, truly metallurgical bounding 

Features:

LOWER COST and HIGHER EFFICIENCY than traditional products

Wear and corrosion resistant, over 4000 endurance hours, 5 times than bi-metal liner

Anti-impact, 10 times than ceramic liner 

Hardness: 70HRC 

Coating bonding: 110MPa

Coating finish: 1-2mm thickness with 0.2-0.3mm substrate infiltration

F 1600/1300 for mud pump liner